High Resilience SCR Neoprene Sheet For Luggage,Phone case, Camera bag,Outdoor gloves, Footwear
Product Details:
| Place of Origin: | China |
| Brand Name: | HuiXinFa |
| Certification: | (EC) NO 1907/2006(REACH) HCT/RF-23-17 |
Payment & Shipping Terms:
| Minimum Order Quantity: | 300sheets |
|---|---|
| Price: | Negotiation |
| Packaging Details: | Packed in rolled |
| Delivery Time: | 10 Working Days |
| Payment Terms: | T/T (30% deposit, 70% before shipment) |
| Supply Ability: | 50,000sheet per month |
|
Detail Information |
|||
| Product Name: | Neoprene SCR | Thickness: | 1.0- 7.0mm Or Customized |
|---|---|---|---|
| Feature: | Shockproof, Keep-warm | Process: | Laminated |
| Usage: | Non-slip,Heating Vest,Belt Type,Oven Glove,bag,Carpet Mats | Hardness: | 0~15° |
| Size: | Width No Less Than 51'' ,Length Customed | Printing: | Available |
| Highlight: | SCR neoprene spandex fabric,12 degree neoprene spandex fabric |
||
Product Description
Orthopedic Product, Sleeves, Tubes, Covers, Supports, Clothes, Shoes, Bikini, Pants, Sport Bra, Gloves, Socks, Hats, Masks...etc.
And all you imaged products.
| Items No. | Items | Color | Hardness (AC) | Denisty (g/cm³) |
Tensile Strength (kg/cm²) |
Elongation at Break (%) | Tear Strength (kg/cm) |
Water Absorption (%) | Compression Set (25% 70°C 22h 30min) (%) |
Thermal Shrinkage (70°C 22h 5%) | Vulcanization Test (100°C 90min) (%) |
Ozone aging test (50°C 3h Ozone concentration 50ppm) |
| 1 | SBR(EJ) | black | 10°~15° | 0.17±0.02 | ≥3 | ≥130 | ≥1.2 | ≤5 | ≤40 | ≤6.5 | ≤8.5 | No cracks on the surface |
| 2 | eco-friendly SBR | black | 10°~15° | 0.20±0.02 | ≥3.2 | ≥170 | ≥1.5 | ≤3 | ≤41 | ≤8.5 | ≤8.5 | No cracks on the surface |
| 3 | Sulfur resistance SBR | black | 10°~15° | 0.20±0.02 | ≥3.2 | ≥170 | ≥1.5 | ≤3 | ≤41 | ≤6.5 | ≤6.5 | No cracks on the surface |
| 4 | Off white SBR | Off white | 10°~15° | 0.15±0.02 | ≥4.2 | ≥200 | ≥1.5 | ≤5 | ≤38 | ≤8 | ≤8.5 | No cracks on the surface |
| 5 | Beige SBR | Beige | 10°~15° | 0.15±0.02 | ≥3.4 | ≥190 | ≥1.3 | ≤5 | ≤42 | ≤7.5 | ≤12 | No cracks on the surface |
| 6 | Aquamarine SBR | Aquamarine | 8°~12° | 0.15±0.02 | ≥2.8 | ≥210 | ≥1.4 | ≤5 | ≤42 | ≤10.5 | ≤13.5 | No cracks on the surface |
| 7 | Extra white SBR | Extra white | 6°~10° | 0.15±0.02 | ≥2.7 | ≥210 | ≥1.3 | ≤5 | ≤41 | ≤10.5 | ≤12 | No cracks on the surface |
| 8 | 15%SCR | black | 2°~4° | 0.16±0.02 | ≥2.9 | ≥240 | ≥1.2 | ≤3 | ≤35 | ≤3 | ≤5 | No cracks on the surface |
| 9 | 30%SCR | black | 0°~3° | 0.14±0.02 | ≥2.6 | ≥310 | ≥1.2 | ≤3 | ≤37 | ≤5 | ≤5 | No cracks on the surface |
| 10 | 100%CR-0003 | black | 0°~3° | 0.20±0.02 | ≥5.7 | ≥560 | ≥2.5 | ≤3 | ≤20 | ≤3 | ≤3 | No cracks on the surface |
| 11 | 100%CR-0305 | black | 3°~5° | 0.20±0.02 | ≥4.9 | ≥480 | ≥2.5 | ≤3 | ≤20 | ≤3 | ≤3 | No cracks on the surface |
| 12 | 100%CR-0507 | black | 5°~7° | 0.20±0.02 | ≥6.4 | ≥450 | ≥3.0 | ≤3 | ≤20 | ≤5 | ≤5 | No cracks on the surface |
| 13 | 100%CR-0911 | black | 9°~11° | 0.18±0.02 | ≥4 | ≥260 | ≥2.6 | ≤3 | ≤25 | ≤15 | ≤10 | No cracks on the surface |
|
Product Name
|
football jacquard knitted fabric Customize Thickness Neoprene fabric
|
|
Material
|
Neoprene SBR, SCR, CR
|
|
Color
|
Black, Cream & White
|
|
Thickness
|
1.0- 7.0mm or customized
|
|
Width
|
50"±1"
|
|
Embossing
|
Available
|
|
Perforated
|
Available
|
|
Printing
|
Available
|
|
Lead Time
|
3-15 working days
|
|
Usage
|
Neoprene Product
|
lycra fabric, light, comfortable,Colorful, environmental friendly, elegant and breathable,High cost performance, wide range of application, It is a kind of common fitting cloth in diving materials. Fabric color can be customized.
FAQ
1. how can we guarantee quality?
Always a pre-production sample before mass production;
Always final Inspection before shipment;
2.what can you buy from us?
Medical Protective Fabric,Health Sports Fabric,Adhesive Cloth Composite Series,Composite Series Of Neoprene Materials,Waterproof And Moisture Permeable Composite Series
3. why should you buy from us not from other suppliers?
We own the advanced compound equipment and professional technist owned rich working experience over 20 years to make sure a good quality. Rich experience in composite and working on constantly improving production quality make new and old customer satisfy.